Microwave assisted synthesis of Mn3O4 nanograins intercalated into reduced graphene oxide layers as cathode material for alternative clean power generation energy device

Scientific Reports volume 12, Article number: 19043 (2022) Cite this article

1573 Accesses

2 Citations

1 Altmetric

Metrics details

Mn3O4 nanograins incorporated into reduced graphene oxide as a nanocomposite electrocatalyst have been synthesized via one-step, facile, and single-pot microwave-assisted hydrothermal technique. The nanocomposites were employed as cathode material of fuel cells for oxygen reduction reaction (ORR). The synthesized product was thoroughly studied by using important characterization, such as XRD for the structure analysis and FESEM and TEM analyses to assess the morphological structures of the material. Raman spectra were employed to study the GO, rGO bands and formation of Mn3O4@rGO nanocomposite. FTIR and UV–Vis spectroscopic analysis were used to verify the effective synthesis of the desired electrocatalyst. The Mn3O4@rGO-10% nanocomposite with 10 wt% of graphene oxide was used to alter the shiny surface of the working electrode and applied for ORR in O2 purged 0.5 M KOH electrolyte solution. The Mn3O4@rGO-10% nanocomposite electrocatalyst exhibited outstanding performance with an improved current of − 0.738 mA/cm2 and shifted overpotential values of − 0.345 V when compared to other controlled electrodes, including the conventionally used Pt/C catalyst generally used for ORR activity. The tolerance of Mn3O4@rGO-10% nanocomposite was tested by injecting a higher concentration of methanol, i.e., 0.5 M, and found unsusceptible by methanol crossover. The stability test of the synthesized electrocatalyst after 3000 s was also considered, and it demonstrated excellent current retention of 98% compared to commercially available Pt/C electrocatalyst. The synthesized nanocomposite material could be regarded as an effective and Pt-free electrocatalyst for practical ORR that meets the requirement of low cost, facile fabrication, and adequate stability.

Day-by-day growing needs, the rapid development of the global economy, and technology have led to the diminution of fossil fuel reserves, resulting in an energy crisis and global warming issues1. Although present energy demands are being met by conventional fossil fuel reserves, these energy sources need to be reserved for future generations2. This looming energy crisis has driven researchers to look for sustainable, cost-effective, environmentally friendly, and efficient alternative energy sources3. Therefore, in search of alternative energy sources, a tremendous amount of effort has been made to find renewable energy sources. Li-Ion batteries, supercapacitors, fuel cells, and solar cells as electrochemical energy storage/conversion devices have gained considerable attention4,5,6,7,8. Rechargeable metal-air batteries (MABs) and proton exchange membrane fuel cells (PEMFCs) are next-generation energy sources for producing clean electricity9,10. In these devices, O2 reduction takes place at the cathode surface. In energy conversion devices (fuel cells), the O2 reduction reaction is a critical process. Oxygen reduction reaction (ORR) happens in two main pathways in an aqueous solution; (1) a four-electron transition that reduces O2 to H2O (water) and (2) a two-electron transfer mechanism where O2 is reduced to H2O2 (Hydrogen peroxide). In the case of aprotic non-aqueous solvents or alkaline solutions, a 1 electron reduction phenomenon can also occur by reducing O2 into superoxide (O2−). In the case of proton exchange membrane (PEM) fuel cell operation, the O2 molecules are reduced at the cathode surface by gaining electrons due to ORR. The O=O bond with an exceptionally strong bonding energy of 489 kJ/mol11 is a powerful bond that is very difficult to break electrochemically. To reduce this energy barrier and the bond activation and cleavage, the assistance of electrocatalysts is highly required.

ORR is a six-time slower process at the cathode surface than that of hydrogen oxidation in an aqueous solution in PEMFCs. This slow O2 reduction arises due to the varied reaction pathways and adsorption/desorption process due to the participation of O-containing intermediate species such as OOH*, O*, and OH*12. Because of this reason, the cathode catalyst requirement is often ten times higher than the anode catalyst requirement for fuel cell applications13. On an industrial scale, conventionally-used Pt-based electrocatalyst for ORR accounts for 36–56% of the total cost of fuel cells14,15. Although the high-cost Pt-based electrocatalyst is a significant concern, another drawback of conventionally-used electrocatalyst is its susceptibility to fuel crossover, due to which the stability of the fuel cell is compromised, hence tremendously limiting the fuel cells’ massive applications. Consequently, creating a highly active, sufficiently stable, and economical electrocatalyst is of supreme importance to replace the Pt-based cathode electrode for large-scale applications.

To develop a cathode of fuel cells that is economical, abundantly available, and has higher performance as an alternative to Pt-based catalyst, researchers have proposed various metal oxides16,17,18, metal sulfides19,20, metal-based materials21,22 in the form of the unary, binary and ternary nanocomposite. It was further discovered that combining the above-discussed cathode material with carbon support can further enhance their activity for ORR because of the supporting material's higher surface area23. In this work, we have developed metal oxide supported on various concentrations of carbon matrix, i.e., reduced graphene oxide (rGO) layers, and exploited for ORR. The synthesized cathode catalyst has rivalled the conventionally used Pt-based catalyst for ORR. This report presents the synthesis of Mn3O4 nanoparticles incorporated into various concentrations (wt%) of GO (5, 10, and 15 wt%) w.r.t. Mn3O4 precursor using the microwave hydrothermal technique.

The microwave hydrothermal technique is a novel powder preparation process that has emerged in recent years. It employs microwaves for heating and operates on the hydrothermal principle; however, it differs from the typical hydrothermal synthesis process. The microwave hydrothermal technology combines hydrothermal and microwave technologies, maximizing the benefits of microwaves and water heating. In contrast to the hydrothermal method, the microwave hydrothermal heating method employs microwaves rather than a single conduction approach. Even if the sample has a certain depth, microwaves may enter it and heat each depth simultaneously, eliminating heat conduction, resulting in a temperature differential, and considerably boosting reaction speed. In comparison to the traditional hydrothermal method, the microwave hydrothermal method has a faster heating speed, a more sensitive reaction, and a more uniform heating system, allowing it to swiftly generate nanoparticles with a consistent particle size distribution and shape24.

A microwave-assisted hydrothermal method is low-cost and eco-friendly, with low environmental impacts and little processing time. The primary advantage of this synthesis process is its efficient energy transfer and fast volumetric heating25 compared to the ordinary hydrothermal methods generally carried out in the conventional heating oven, which cost longer synthesis time and slow process. The microwave-assisted hydrothermal method is a low-energy consumption method with high yield and selective heating26. Furthermore, the nanocomposite synthesized via microwave-assisted hydrothermal method consists of multiple characteristics that include a high yield, facile preparation method, single step, and low energy consumption27,28,29,30.

Graphene-based nanocomposite synthesized by microwave-assisted hydrothermal process has attracted intensive attention nowadays from researchers for various applications31. The use of microwaves in hydrothermal synthesis has great applicability when making carbon-based material due to their microwave absorbance. Using the microwave-assisted synthesis for graphene-based nanocomposite can promote various reactions, including synthesis of desired material/nanocomposite, reduction and exfoliation of graphene, doping, wrapping, and decoration of metal/metal oxides to the graphene surface32. The novel composite electrode material synthesized by microwaves assisted method based on graphene derivatives containing metals/metal oxides has shown great applicability and improved performance for electrochemical applications. This method of synthesis helps the metal/metal oxide material to be anchored, intercalated, and wrapped into various layers of carbon materials (rGO in this case), which eventually promotes faster electron transfer, higher surface area and also allows the electrolyte to interact and diffuses into the sample layers33. The slight changes in microwave power, reaction time and variation of solvent and additives can help in the synthesis of material with diverse morphologies and characteristics of the synthesized material34. Based on the facts explained, we have preferred to use the hydrothermal synthesis method for Mn3O4@rGO nanocomposites for ORR activity.

To date, numerous carbon-based metal oxide nanocomposite materials have been developed and employed for various energy related fields35,36,37, specifically for ORR3,38,39. Most of the reported work mainly focused on the application part by using complicated synthesis techniques which involved various steps and more chemistry40,41,42,43. The main goal of this project was to develop a composite material with versatile features and comparable performance for ORR as presented by the Pt/C electrocatalyst. Therefore, aiming this idea in mind, we have used a very practical, facile, reproducible, and faster synthesis technique based on the microwave-assisted hydrothermal method. Employing the microwave-assisted hydrothermal method, we have synthesized the electrocatalyst for energy application which is 36 times quicker than we reported earlier3. Hence the microwave-assisted hydrothermal method is a highly recommended, reliable, time and energy-saving method for various technological applications. The Mn3O4@rGO nanocomposites synthesized by using the microwave-assisted hydrothermal method have shown greater stability, low overpotential values, well defined higher O2 reduction peaks for fuel cell applications.

The Mn3O4@rGO nanocomposite was synthesized for ORR in an alkaline medium. Alkaline media for non-Pt-based electrocatalysts provides a suitable environment for ORR without affecting the catalyst performance, with no detrimental effects and less corrosivity44. The as-synthesized Mn3O4@rGO nanocomposites were characterized sufficiently by employing XRD, TEM, FESEM, EDX mapping, FTIR, BET, Raman, two probe conductivity tests, and UV–vis techniques. The electrochemical study of nanocomposite was investigated as cathode material of fuel cells for ORR, and methanol tolerance was studied by injecting a higher concentration of CH3OH molecules into the electrochemical cell. The stability study of the nanocomposite is also conducted in comparison with the conventionally used commercially available Pt/C electrocatalyst for ORR.

The chemicals and reagents purchased were of analytical quality and used as it is without any further purification. For the synthesis of desired electrode material, Graphite flakes were obtained from Asbury Graphite Inc., Rodeo (USA). The following chemicals were bought from R & M Chemicals, Selangor, Malaysia: sulfuric acid, 98%; phosphoric acid, 88%; hydrochloric acid, 35%; potassium permanganate, 99%; and ammonia solution, 25%. We bought potassium hydroxide and manganese (II) acetate tetrahydrate from Sigma Aldrich, Malaysia. Hydrogen peroxide (H2O2 35%) and methanol (CH3OH) were acquired, Malaysia as well. All of the experimental work was done with DI water.

The Simplified Hummer's technique was adopted for graphene oxide (GO) synthesis45. In brief, 3 g of graphite flakes were mixed and dissolved in H2SO4 and H3PO4 (9:1) mixture under a continuous stirring process. Afterwards, KMnO4 (18 g) was added to the subject solution very slowly under stirring by continuously monitoring the temperature. The solution was then left under stirring for three days with proper monitoring for complete oxidation of graphite flakes. After three days, an H2O2 solution containing ice was added to the above mixture to quench the reaction considering that 3 days were enough for oxidizing graphite. After adding H2O2, the dark green color solution turned into a yellow color solution, indicating a higher level of graphite oxidation. The washing process was conducted, and the oxidation stopped by using 1 M HCl solution, followed by a rigorous and long washing process with DI water to remove the acid from the resulting product and reach a pH of 5 to 6. An ultra-high speed centrifugation procedure was used to wash supernatants for decantation, which also helped in the exfoliation of graphite oxide into multi-layered GO gel. The synthesized GO solution was further used for the preparation of electrode material of fuel cell with Mn3O4 as composite. The prepared GO solution was diluted to 1 mg/ml concentration and sonicated to exfoliate further the stacked layer of GO, followed by again centrifuging to collect the supernatant by leaving the multi-layer GO at the bottom. In detail, 1 mmol of Mn(CH3CO2)2·4H2O precursor prepared in 15 ml of DI water solvent was slowly added dropwise with a rate of 1 drop/sec into the different wt% (5, 10, 15 wt%) of GO solution under a continuous stirring process. Slowly adding Mn(CH3CO2)2·4H2O precursor solution into GO provides sufficient time for Mn ions to bond electrostatically with GO functional groups to make nanocomposites. The prepared solution was kept under stirring for 2 h to give the mixture a maximum time so that the reaction between the precursor solution and GO could happen. After that, a low concentration of ammonia (6%) solution was dropwise added to the mixture to achieve a basic pH (of 10). The ammonia solution will support the conversion of GO to rGO and the precipitation of manganese ions46,47,48. The Teflon tubes of 100 ml was filled with the prepared mixture up to 75%, appropriately sealed and placed into a microwave digester for hydrothermal reaction. The mixture was kept under reaction conditions for about 20 min at 180 °C. After the completion of reaction, the synthesized product was allowed to cool down, and the precipitates were then collected, washed with DI water and ethanol, and adequately packed. After the washing process, the product was dried, crushed, and stored for further analysis. The exact process was repeated for the rest of the nanocomposites by varying the GO wt%. The same experimental procedures were also used to create the control samples. The prepared nanocomposites were named Mn3O4@rGO-5%, Mn3O4@rGO-10%, and Mn3O4@rGO-15%, respectively. The schematic in Fig. 1 show the steps of Mn3O4@rGO nanocomposites synthesis.

The steps of Mn3O4@rGO nanocomposites synthesis. Illustrations were generated using ChemSketch, version 2021.1. 2 and Vesta software.

The phase identifications of as-synthesized samples were performed on a Bruker D8 advance using copper Ka radiation (λ = 1.5418 nm) under 40 kV and 40 mA with a scan rate of 0.02-degree sec−1. The morphological and structural properties of the prepared samples were analyzed by SEM and TEM on a Hitachi SU8030 with an acceleration voltage between 3 and 10 kV, fitted with an EXD mapping tool and JEOL :JEM2010 respectively. Raman spectra were taken using SENTERRA Dispersive Raman Microscope by Bruker with a laser excitation wavelength of 532 nm. UV–Vis and FTIR measurements were conducted on a Thermo Scientific GENESYS 180 spectrophotometer and Thermo Scientific Nicolet iS5 with a diamond crystal ATR, respectively.

The electrochemical performance of Mn3O4@rGO nanocomposites electrode with various GO concentrations was evaluated towards ORR. A glassy carbon electrode (GCE) modified with catalyst ink was employed as a working electrode for ORR measurement. GCE's surface was physically polished using 0.05 mm alumina polishing paste before modification. Additionally, GCE was electrochemically cleaned in a 0.5 M H2SO4 solution with a potential range of − 1 to 1 V for about 100 cycles to remove any adsorbed material on the GCE surface, followed by a 5 min sonication. The mirror-like polished surface of the GCE (D = 3 mm) was dropped cast with a catalyst ink of 5 μL and 1 mg/ml concentration, and was then dried at ambient temperature for electrochemical studies.

The electrochemical studies were performed in a typical three-electrode electrochemical cell at room temperature using a Versa stat 4F potentiostat/galvanostat from Princeton Applied Research. The modified GCE served as a working electrode, whereas the reference and counter electrodes were SCE and Pt wire, respectively. A 0.5 M KOH was used as an electrolyte solution, and all electrochemical tests were performed at room temperature. The cyclic voltammetry studies were taken at the potential range from 0 to − 0.8 at a scan rate of 50 mVs−1. Scan rate studies, stability tests, and tolerance of electrocatalysts were also evaluated and explained in detail in the results and discussion.

XRD patterns of Mn3O4 nanoparticles and Mn3O4@rGO nanocomposites are shown in Fig. 2. All characteristic peaks of Mn3O4 agree well with the standard data of Mn3O4 (COD #1514121) with the space group I41/amd49. No impurities were observed in the XRD patterns of both bare Mn3O4 and Mn3O4@rGO nanocomposites. Furthermore, the crystal phase of rGO was not observed, this might be due to the amorphous nature of rGO, and the smaller Mn3O4 might have completely covered the surfaces of layered rGO, which causes a low degree of graphitization.

XRD patterns of (a) Mn3O4, (b) Mn3O4@rGO-5%, (c) Mn3O4@rGO-10%, and (d) Mn3O4@rGO-15%, and the standard data of Mn3O4 from COD database #1514121.

The diffraction pattern of Mn3O4 is observable in all composites with different wt% of GO contents. Strong crystalline peaks of the pure Mn3O4 were observed at 2θ values and their corresponding crystal planes of 18.0° (011), 28.9° (112), 31.0° (020), 32.3° (013), 36.1° (121), 38.0° (044), 44.4° (220), 49.9° (024), 50.7° (015), 53.9° (132), 56.0° (033), 58.5° (231), 59.8° (224), 64.6° (040) and 74.2° (143). Correspondingly, the amount of Mn3O4 in the composite led to an increase in the diffraction peaks' intensity. Mn3O4@rGO-15% composite shows the highest intensity, while Mn3O4@rGO-5% shows the least. The Debye–Scherrer equation was used to calculate the crystallite size from the peak width is as follows50:

where D denotes crystal size, and B is a value of FWHM of selected peaks. In order to determine the values to estimate crystal size, the Gaussian function was used to fit diffraction peaks. The average particle sizes of bare Mn3O4, Mn3O4@rGO-5%, Mn3O4@rGO-10%, and Mn3O4@rGO-15% are 33.29, 29.97, 29.10, and 29.49 nm, respectively.

The morphological structures of the composites were inspected using FESEM analysis techniques fitted with EDX mapping, as shown in Fig. 3. Mn3O4 nanoparticles showed granular structures. Highly aggregated Mn3O4 nanoparticles were observed as it is widely recognized that metal oxide nanoparticles precipitate in agglomerated form after a hydrothermal process. Due to the agglomerated nature of Mn3O4 nanograins-based semiconductors, the electrocatalytic reduction of O2 suffered from low ion transportation problems, as can be seen through the electrochemical studies in Fig. 9. The incorporation of carbon matrix in the form of rGO without disturbing the morphological structure of Mn3O4 has significantly reduced the agglomeration and helped in electrons transfer facilitation at the interface of Mn3O4@rGO-10% nanocomposite modified GCE and electrolyte (Fig. 3C) therefore played a crucial role in the ORR. It can be observed through Mn3O4@rGO nanocomposites presented in Fig. 3B–D that Mn3O4 is sandwiched between various layers of rGO sheets. Therefore, blurry images of Mn3O4 nanograins were observed under rGO sheets, as circled in FESEM images. These sandwiched nanoparticles behave like spacers between the various rGO layers by letting the electrolyte diffuse into multiple nanostructure layers, resulting in an enhanced electrocatalytic activity. The nanocomposites Mn3O4@rGO-5% and Mn3O4@rGO-15% were also studied under FESEM. Mn3O4@rGO-10% (Fig. 3B) showed higher improved performance than other concentrations of GO for ORR, reflecting an optimum concentration of GO. The Mn3O4@rGO-5% nanocomposite containing 5 wt% of GO remains unsuccessful in preventing the agglomeration of Mn3O4 due to lower GO contents. This results in lower electrocatalytic performance for ORR. Moreover, a higher concentration of GO up to 15 wt% led to a higher number of transparent rGO sheets, which effectively decreased the concentration of the Mn3O4 catalyst. Hence, lower electrocatalytic performance was observed in the case of Mn3O4@rGO-15% for ORR (Fig. 3D).

FESEM images of (A) Mn3O4, (B) Mn3O4@rGO-5%, (C) Mn3O4@rGO-10%, and (D) Mn3O4@rGO-15%.

TEM analysis was used to analyze the nanostructures of Mn3O4 and Mn3O4@rGo nanocomposites. Figure S1 clearly shows the agglomerated nanosized particle of unaided Mn3O4 nanograins after microwave-assisted hydrothermal synthesis, which is evident for metal oxide nanoparticles without any supporting matrix. Figure S1B–D distinctly shows the rGO (marked by arrows) supported Mn3O4 nanograins from bare Mn3O4 nanograins. The densely populated nanograins of Mn3O4 on the rGO surface in Figure S1(B) are due to the lowered concentration of GO (5 wt%) initially used for synthesizing nanocomposites. While figure S1(D) reveals that the less populated Mn3O4 nanograins distributed evenly on the rGO matrix are due to increased layers of rGO and confirms the highest concentration of GO used for the synthesis of Mn3O4@rGO-15% nanocomposites. At the same time, the optimized and balanced distribution of Mn3O4 nanograins was observed in figure S1(C) with 10 wt% of GO used for the synthesis of Mn3O4@rGO-10% nanocomposites. The TEM images have the same chemistry as explained in the FESEM images and the XRD analysis. Hence the TEM agreed well with the XRD and SEM analysis. The particle size of the Mn3O4@rGO nanocomposite was calculated using ImageJ software, and the average particle size was found to be 32 nm by considering 200 particles, which is in good agreement with the XRD results.

EDX was used to inspect the elemental distribution and purity of Mn3O4@rGO-10% nanocomposite, as shown in Fig. 4. The EDX spectrum showed prominent peaks related to Mn (64.94%), O (23.05%), and C (11.18%) without traces of other peaks, confirming the purity of the synthesized nanocomposite. The peak of Si (0.82%) was likely aroused from the substrate. The C peaks are related to the presence of rGO in the nanocomposite. The elemental distribution of unaided Mn3O4 nanograins was also tested using EDS, as shown in figure S2. The carbon-coated Cu grid was used for the EDS analysis, and the EDS spectrum shows the prominent peaks with atomic % related to the O and Mn with 50.66 and 34.32, respectively (inset figure S2). The wt% of Mn and O was also recorded and found as 61.4 and 26.4, respectively, without any extra peaks related to the involvement of impurities during the synthesis.

EDX analysis of Mn3O4@rGO-10% nanocomposite.

To validate the presence of each element, an element mapping analysis was performed, and the distribution of each component of the nanocomposite electrode materials is shown in Fig. 5. The combined elemental distribution ensures a homogeneous distribution of all elements in the nanocomposite of Mn3O4@rGO-10% (Fig. 5B). The mapping was derived from the FESEM image to analyze elemental distribution, as seen in Fig. 4A. The high density of yellow dots in Fig. 5F represents the densely distributed Mn nanoparticles on the carbon matrix (red color). In contrast, the green color represents the presence of oxygen in Mn3O4 nanoparticles (Fig. 5D). The purple color mapping image reflects the presence of the Si substrate used for analysis purposes (Fig. 5E). The presence of carbon as red color dots in Fig. 5C confirms the presence of rGO matric in the nanocomposite.

EDX elemental mapping images of Mn3O4@rGO-10% nanocomposite, (A) FESEM image, (B) Mix, (C) Carbon, (D) Oxygen, (E) Si wafer, and (F) Mn.

Figure S3 (A &B) shows the Raman spectra of two fundamental vibrations ranging from 1100 to 1700 cm−1 for GO and rGO. The D band formed due to the breathing mode of j-point photons is visible at 1356.8 and 1351.12 cm−1 belonging to the A1g symmetry of GO and rGO, respectively51. However, in figure S3(B), the first ordered scattered G vibration band belongs to E2g phonons by sp2 carbon having peaks appearing at 1591.79 cm−1 belongs to GO and 1597.3 cm-1 for rGO52. Furthermore, the existence of the stretching C–C bond, which is typical for all sp2 carbon systems, also contributed to originating off the G vibration band in GO and rGO spectrums53. In the Raman spectrum, the disorder bands are represented by the D band, and the G band refers to tangential bands52. The 2D band is used to determine monolayer bilayer and multilayer graphene sheets and is very sensitive to stacking graphene layers. The shifted 2D band at 2694.93 cm−1 in figure S3B confirms a multilayer GO synthesis. Further, the shift in wavenumber for GO was also due to the presence of oxygen-containing functional groups, which helps to prevent the GO layer from stacking. Moreover, the 2D band for rGO appeared at a lower wavenumber (2686.32 cm−1) as compared to GO due to the reduction of GO into rGO and the presence of less number of oxygen functional groups, which causes the rGO layer to restack51.

The lower intensity ratio of the D to G band (0.87 < 1) shows the successful synthesis of GO, while after the microwave synthesis, the GO was reduced to rGO54, confirming the restoration of sp2 carbon, which resulted in higher D to G intensity ratio (ID/IG > 1) and higher intensity of D band due to the removal of oxygen function moieties55. Figure S3(C) shows the Raman spectra of the Mn3O4@rGO-10% nanocomposite; the appearance of Raman modes in the range of 100–1000 cm−1 along with D, G, and 2D bands confirms the successful synthesis of nanocomposites. However, the high-intensity band at wavenumber 657.6 cm−1 refers to the A1g mode due to oxygen ions motion inside MnO6 octahedra and is attributed to Jahn–Teller distortion. Besides this, the band with low-intensity peaks located at 372 and 319 cm-1 corresponds to the Mn–O bending modes and oxygen bridge species of asymmetric stretch (Mn–O–Mn), respectively56. Besides this, a shallow intense peak at 466.5 cm−1 appeared to be assigned to the Eg mode of Raman.

UV–Vis spectroscopy was used to examine the reduction of GO into rGO during a microwave hydrothermal process, as illustrated in Fig. 6A. The Soret band red shift was observed for rGO at 272 nm after the microwave hydrothermal reaction, indicating a more significant number of electron transfers from the rGO sheets. The inset in Fig. 6A shows a sharp GO peak at 229 nm for the π–π* transition of C–C bonds51. A fragile shoulder that appeared at 300 nm in the GO spectrum is associated with C=O bonds, which is consistent with the n-π* transition and supports the presence of the carbonyl group on the GO surface57,58. UV–Vis spectrum of Mn3O4 and rGO nanocomposite (Fig. 6B demonstrates the absorbance band of rGO at 220 nm, including the hump of Mn3O4 catered about 430 nm (Fig. 6B(inset), indicating the formation of Mn3O4@RGO nanocomposite. The inset in Fig. 6B shows that Mn3O4 exposes the lowest UV absorption regime and shows an absorption spectrum as a hump centered at around ~ 430 nm59,60.

(A) UV–Vis spectra of rGO and GO (Inset), and (B) Mn3O4@rGO-10% nanocomposite with Mn3O4 as inset.

The chemical compositions of GO, Mn3O4, and Mn3O4@rGO-10% nanocomposites were investigated employing FTIR spectroscopy, as shown in Fig. 7. In Fig. 7A, due to the O–H stretching vibration of intercalated water, a wide band for GO emerged about 3192 cm−161. The band at 1729 cm−1 is allocated to the C=O stretching mode of carboxylic acid and carbonyl moieties. In addition, the band at 1612 cm−1corresponds to the unoxidized graphitic domain61 or C=C bond of sp2 hybridized stretching vibration. The band at 1378 cm−1 was attributed to the stretching vibrations of C–OH62,63, and the shoulder bands appeared at 1176, and 1043 cm−1 are attributed to C–O epoxy starching and C–O alkoxy stretching, respectively3,64,65,66. Figure 7B shows characteristic bands between 400 to 600 cm−1 assigned to the stretching modes of Mn–O67. The band located at 594 cm−1 is attributed to the Mn–O stretching mode of tetrahedral sites, while the 474 cm−1 band is related to the distortion vibration of Mn–O at the octahedral sites. The band appearing near 400 cm−1 is likely attributed to the Mn vibrations in the Mn3O4 octahedral site68. The corresponding spectrum of Mn3O4@rGO-10% nanocomposite shows similar characteristic bands to those of Mn3O4 without extra absorption bands related to GO, indicating the reduction of GO to rGO in the nanocomposite was successful.

ATR-FTIR spectra of (A) GO and (B) Mn3O4 and Mn3O4@rGO-10% nanocomposite.

The electrical conductivity of all nanocomposites and Mn3O4 was measured by the two-probe method at room temperature by making pellets of the synthesized samples. Various data points were collected by selecting different positions on the pellets, and values are summarized in Table 1. The nanocomposites of Mn3O4@rGO have exhibited higher electrical conductivity for the increasing contents of rGO. Mn3O4 being an insulator has shown overflow and hence presented zero conductivity. On the other hand, the conductivity increased for Mn3O4@rGO-15% > Mn3O4@rGO-10% > Mn3O4@rGO-5%, summarized in Table 1. This increased conductivity was basically due to the higher wt% of GO used for the synthesis of nanocomposite, which resulted in rGO contents after reduction by microwave hydrothermal reactions. Basically, rGO is the source of electrical conductivity to the intercalated nanograins of Mn3O4.

The redox behavior of [Fe(CN)6]3-/4- was studied at the nanocomposite-modified GCE, including other controlled electrodes. This is a valuable technique for studying the kinetic barrier at the interface of a modified electrode and the electrolyte. The transfer of electrons at the electrode interface and the electrolyte solution occurs due to tunnelling from the defects present in the barrier or through the barrier69,70. Therefore, [Fe(CN)6]3-/4- redox couple was selected as a standard marker to study the change in behavior of different synthesized cathode materials, as it is a frequently used diagnostic tool for elucidating the mechanism of modified electrodes. Considering the redox chemistry viewpoint, using ferricyanide or ferrocyanide as a redox couple is a one-electron transfer phenomenon at room temperate. As can be seen through Fig. 8A in the forward scan of CV at bare GCE/Modified GCE surface, the ferrocyanide is oxidized and converted into ferricyanide by donating one electron. During the cathodic sweep or reverse scan, ferricyanide reduction started and reverted to ferrocyanide by accepting one electron. This continuous process shows that the ferricyanide/ ferrocyanide redox reaction is a single electron transfer process71,72.

(A) Cyclic voltammetric curves taken for Bare GC, rGO, Mn3O4, and Mn3O4@RGO nanocomposite with different wt% of GO (5%, 10%, and 15%) modified GCE in 1 mM K3[Fe(CN)6] as analyte in 0.1 M KCl electrolyte at a scan rate of 50 mVs−1, (B) the EIS studies are taken into the exact solution for bare GCE and Mn3O4, (C) rGO and Mn3O4@rGO-10% nanocomposite modified GCE.

Figure 8A shows the results from various electrode materials using cyclic voltammetry in 0.1 m KCl as electrolyte solution and 1 mM ferricyanide as analyte at a scan rate of 50 mV/s.

The bare GC electrodes showed a well-defined CV with a diffusion-limited redox process. After modifying the GC electrode surface, the redox peak current increase gradually on the order of Mn3O4@rGO-10% > Mn3O4@rGO-15% > Mn3O4@rGO-5% > Mn3O4 > rGO due to the facilitation and tunnelling of a more significant number of electrons through the defects or the barrier. This is due to the conductivity of rGO (in the composite) and the contribution of evenly distributed Mn3O4 nanograin electroactive surface area on rGO sheets, which facilitate more significant and faster electron transfer numbers. Noticeably, the peak potential separation (ΔE) decreased with the increase in the redox current for Mn3O4@rGO-10%, compared to other controlled electrodes. The decrease in the anodic and cathodic peak currents by Mn3O4@rGO-15% nanocomposite was also observed compared with Mn3O4@rGO-10% nanocomposite. The increasing number of rGO sheets is predicted to reduce the density of the Mn3O4 nanoparticles, which coincides with the FESEM picture in Fig. 3.

The EIS studies were also carried out in line with the cyclic voltammograms in ferricyanide containing KCl electrolyte at the frequency ranges from 0.01 to 100 000 Hz to investigate the charge transfer facilitation at the interface of the modified GCE and the electrolyte (Fig. 8B and C)). The Nyquist diagram shows the real (Z’’) versus imaginary (Z’) components of the complex impedance with a semicircle showing the charge transfer resistance at higher frequencies and the straight line corresponding to the diffusion-limited process in the low-frequency region73. The GC electrode shows a higher Rct value of 30 K Ω, compared with the Mn3O4 modified GC electrode (Rct = 25.875 K ohm) by following the trajectory of the semicircle at high frequencies. This confirms the resistance at the electrode and electrolyte interface, which hinders the flow of charges. The Mn3O4@rGO-10% and rGO-modified GC electrode was investigated. No semicircle was formed for both the modified electrodes, showing the lowest charge transfer resistance and faster electron transfer. The straight light adjoining the semicircle for all electrodes shows the Warburg impedance of all electrodes at higher frequencies. The Warburg impedance with an angle slightly more elevated than 45° represents that the electrode doesn't behave like a capacitive material74.

The electrochemical behavior of modified GCE with all the synthesized electrode material was examined for ORR as fuel cell application in an O2-saturated 0.5 M KOH (Fig. 9A). The cyclic voltammetric approach was applied at a scan rate of 50 mV/s for O2 reduction within the potential range of 0.0 to − 0.8 V. All controlled electrodes were also employed in the ORR activity. The bare GCE contributed a very low current density peak of 0.266 mA/cm2 when compared with Mn3O4 modified GCE (− 0.448 mA/cm2) with a low overpotential of − 0.358 V. The rGO being a conducting 2D material with extraordinary electrical and electronic properties, has performed better than the Mn3O4 modified and bare GCE with a current density of -0.562 mA/cm2 but with a slightly higher overpotential value of -0.395 V due to the restacked wrinkled sheets after reduction of GO into rGO. The unaided Mn3O4 nanoparticle has shown poor electrocatalytic performance due to the agglomerated nature of metal oxides when compared with Mn3O4@rGO nanocomposites. The electrocatalytic activity was dramatically increased for ORR when nanocomposite-modified GCE was employed in O2 saturated KOH electrolyte. The Mn3O4 nanoparticles and the high conduction rGO in the nanocomposites have contributed to higher electrocatalytic performance with a current density of − 0.738 mA/cm2 shown by Mn3O4@rGO-10% nanocomposite. It was due to the synergistic effect, which helped shift potential towards a positive side at the value of − 0.345 V and a well-defined peak of ORR75. It is well known that the removal of oxygen functional groups causes the layers of rGO to stack after reduction by the hydrothermal process. Therefore, as alone do not perform very well.

Cyclic voltammetry curves of (A) Bare GCE, Mn3O4, rGO, Pt/C, and Mn3O4@rGO-10% in O2 saturated 0.5 M KOH at a scan rate of 50 mV/s, (B) the CV comparison of Mn3O4@rGO nanocomposite with other GO wt% (5%,10%, and 15%) in O2 saturated KOH under the same conditions.

Similarly, metal oxide nanoparticles also exist in aggregated form after synthesis, due to which their participation in electrochemical reactions becomes limited76. Using rGO as conducting platform for metal oxide nanoparticles can prevent agglomeration and aggregation. In return, the metal oxide nanoparticle prevents the rGO layers from stacking, and behaves as spacers between the layers of rGO. This synergistic effect of metal oxide nanoparticles and rGO can tremendously boost the performance of electrocatalysts for ORR77. Mn3O4 and rGO nanocomposite was synthesized by considering the same phenomenon. This helps in increasing the overall geomaterial surface area of Mn3O4 by preventing them from agglomeration and, at the same time, spacing between the rGO layers due to the intercalation of Mn3O4 nanoparticles. This helps the electrolyte to diffuse into the various layer of rGO by increasing the electrochemically active surface area and boosts the ORR performance of the cathode material. The commercially available Pt/C catalyst was also exploited for the ORR performance as it is the commonly used electrocatalyst in fuel cells studies, which shows the current density of − 0.536 mA/cm2 at a higher overpotential of − 0.414 V. Besides, as can be seen through Fig. 9B that Mn3O4@rGO-5% and Mn3O4-rGO-15% nanocomposite was also studied by dipping into the O2 saturated KOH as an electrolyte solution. It was noticed that Mn3O4@rGO nanocomposite-modified GCE with 5 and 15 wt% of GO contents showed lower electrocatalyst performance as compared to Mn3O4@rGO-10% nanocomposite, reflecting the optimized contents of GO wt% for ORR studies. The nanocomposite with 5 wt% of GO contents has shown poor performance due to the availability of less active catalytic sites. Further, it was also observed that increasing the content of GO up to 15 wt% also hinders the performance of the electrode material due to an increase in the number of layers which increases the thickness of the diffusion layer3. The higher GO contents are responsible for lower Mn3O4 nanograins density, influencing the electrochemically active surface area. This hinders the electron transfer at the interface of electrode and electrolyte, which is also confirmed by the EIS and CV results carried out in ferricyanide redox couple contained in KCl as electrolytes solution.

Similar work has been done previously by using manganese oxide and reduced graphene oxide nanocomposite as the primary electrode material for ORR in fuel cells and other energy conversion devices. Table 2 here summarizes the reduction of O2 with various parameters and compares the analytical performance of the present nanocomposite with the reported work. The current work displayed satisfactory performance compared with the reported work and stands for its rapid and time-saving one-pot microwave-assisted hydrothermal synthesis for developing cathode material.

The cyclic voltammograms were taken at different scan rates for ORR using Mn3O4@rGO-10% nanocomposite modified GCE in 0.5 M KOH electrolyte solution (Fig. 10A). There is an obvious increase in cathodic peak current that can be seen with increased scan rate. The peak current for ORR corresponding to the square root of scan rates has shown a linear relationship in Fig. 10B. The increase in the reduction current of O2 by increasing the scan rate from 10 to 300 mV/s at nanocomposite-modified electrodes suggested that it is a diffusion-controlled process2. The scan rate studies reveal that the reduction peak current increases with the increase in the scan rate. Meanwhile, it was observed that the oxidation peaks also appear with very weak and broad peaks. From the CV measurements, it is confirmed that the ratio of reduction peak current and oxidation peaks current (ipc/ipa) is decreasing with the increase in scan rate (Fig. 10C). The peak's potential difference ΔEp through the cyclic voltammogram is increasing with the increase in scan rate (Fig. 10D). These observations collectively confirm that the ORR process is quasi-reversible and suggest two electrons transfer at the surface of the modified electrode, which led to the reduction of O2 into the formation of OH2- in alkaline media as expressed in the following Eq. 184. As expressed in the chemical reaction in Eq. 2, the peroxide ions (\({\text{HO}}_{{2^{ - } }}\)) are either obtained by further reduction (Eq. 2) or by the catalytic breakdown of peroxide ions (Eq. 3)85.

(A) Cyclic voltammetry taken at Mn3O4@rGO-10% modified GCE at different scan rates (10–300 mVs−1) in O2 saturated 0.5 M KOH, (B) the calibration plot of the square root of scan rate vs cathodic current, (C) plot of (ipc/ipa) vs. scan rate, (D) plot of DEp vs. scan rate.

The electron is transported from different rGO layers when it reaches Mn ions. This would create high positive charges on the surface of the Mn3O4@rGO-10% nanocomposite. These electrons cause an unbalanced charge distribution, which greatly prefers to adsorb the O2 and increases the rate of the gas diffusion process. Since Mn3O4 nanoparticles firmly adhere to a highly conducting rGO surface, this leads to efficient ionic and larger electron transportation85,86,87.

Methanol tolerance is the key factor to discuss in fuel cell applications, especially in ORR. Because using methanol as a fuel in DMFC, the methanol gas can permeate to the cathode chamber and poison the catalyst due to cross-over effects which significantly reduces the performance of the catalyst. The methanol tolerance was evaluated using Mn3O4@rGO-10% nanocomposite-modified GCE electrocatalyst in the presence of a higher concentration (0.5 M) of CH3OH in O2-saturated 0.5 M KOH (Fig. 11). The comparison of the cyclic voltammograms is shown in Fig. 11 in the presence and absence of CH3OH, which shows that the CV remains unchanged even in the presence of a higher concentration. These results show that the electrocatalyst is highly selective towards ORR and not susceptible to any foreign molecules.

Cyclic voltammograms were taken at Mn3O4@rGO-10% nanocomposite modified GCE in 0.5 M O2 saturated KOH at a scan rate of 50 mVs−1 in the presence and absence of 0.5 M CH3OH.

The stability of Mn3O4@rGO-10% nanocomposite-modified GCE was studied by recording a long-term chronoamperometric (CA) current time (i-t) curve in an O2-saturated KOH solution (Fig. 12). The i-t curve was recorded for Mn3O4@rGO-10% and Pt/C at a potential recorded from the reduction peaks of the cyclic voltammetric curve to obtain the stability curve. It was noticed that even after over 3000 s, the Mn3O4@rGO-10% nanocomposite curve remained unchanged and maintained high current retention of 98% without any susception by the surrounding environment. On the other hand, the CA obtained for Pt/C has loosened its current retention to 58% after 3000 s, which was a 29-time higher decrease compared to Mn3O4@rGO-10% nanocomposite. These results revealed that Mn3O4@rGO-10% is a highly durable catalyst for ORR.

For stability analysis, the Chronoamperometric (i-t) curves of Mn3O4@rGO-10% nanocomposite and Pt/C catalyst-modified GCE in O2 saturated 0.5 M KOH solution.

In summary, the composite of Mn3O4@rGO nanocomposites was produced by the microwave-assisted hydrothermal method, which is a simple, fast, and scalable synthesis method. Mn3O4 and rGO, when combined as hybrid materials, exhibited surprising ORR activities in an alkaline medium. The synthesized nanograins of Mn3O4 were evenly distributed on the rGO matrix. The functional group present on GO matrix prevented the Mn3O4 nanograin from aggregation, and intercalation of Mn3O4 nanograins further helped avoiding the rGO sheets from restacking behaving as spacers and hence resulted in higher ORR activity. The Mn3O4@rGO-10% nanocomposite has shown the highest ORR activity with a current density of − 0.738 mA/cm2 at the shifted potential of − 0.345 V. The tolerance against a higher concentration of methanol was tested by CV, which was present in O2-saturated KOH; it was noticed from CV curves that Mn3O4@rGO-10% nanocomposite exhibited outstanding performance, and it was confirmed that the methanol crossover would not hamper the fuel cell performance. The stability test was conducted using a chronoamperometric technique for 3000 s. It was found that Mn3O4@rGO nanocomposites showed far exceeding stability and durability when compared with commercially available Pt/C catalysts. According to the findings, the microwave-assisted hydrothermal technique of nanocomposite synthesis is an efficient method of producing advanced electrode materials for numerous energy related fields.

http://www.crystallography.net/cod/1514121.html.

Huang, Q. et al. Spinel CoFe2O4/carbon nanotube composites as efficient bifunctional electrocatalysts for oxygen reduction and oxygen evolution reaction. Ceram. Int. 47(2), 1602–1608 (2021).

Article CAS Google Scholar

Shahid, M. et al. A glassy carbon electrode modified with tailored nanostructures of cobalt oxide for oxygen reduction reaction. Int. J. Hydrogen Energy 45(38), 18850–18858 (2020).

Article CAS Google Scholar

Shahid, M. M. et al. Cobalt oxide nanocubes interleaved reduced graphene oxide as an efficient electrocatalyst for oxygen reduction reaction in alkaline medium. Electrochim. Acta 237, 61–68 (2017).

Article CAS Google Scholar

Sagadevan, S. et al. Reduced graphene/nanostructured cobalt oxide nanocomposite for enhanced electrochemical performance of supercapacitor applications. J. Colloid Interface Sci. 558, 68–77 (2020).

Article ADS PubMed Google Scholar

Ahmed, U. et al. An efficient platform based on strontium titanate nanocubes interleaved polypyrrole nanohybrid as counter electrode for dye-sensitized solar cell. J. Alloy. Compd. 860, 158228 (2021).

Article CAS Google Scholar

Alizadeh, M. et al. Cu2O/InGaN heterojunction thin films with enhanced photoelectrochemical activity for solar water splitting. Renew. Energy 156, 602–609 (2020).

Article CAS Google Scholar

Ehsan, M. A. et al. Fabrication of CuO–1.5 ZrO 2 composite thin film, from heteronuclear molecular complex and its electrocatalytic activity towards methanol oxidation. RSC Adv. 5(126), 103852–103862 (2015).

Article ADS CAS Google Scholar

Geng, H. et al. Metal coordination polymer derived mesoporous Co3O4 nanorods with uniform TiO2 coating as advanced anodes for lithium ion batteries. Nanoscale 8(5), 2967–2973 (2016).

Article ADS CAS PubMed Google Scholar

Ioroi, T. et al. Electrocatalysts for PEM fuel cells. Adv. Energy Mater. 9(23), 1801284 (2019).

Article Google Scholar

Fu, J. et al. Electrically rechargeable zinc–air batteries: Progress, challenges, and perspectives. Adv. Mater. 29(7), 1604685 (2017).

Article Google Scholar

Li, Y. & Dai, H. Recent advances in zinc–air batteries. Chem. Soc. Rev. 43(15), 5257–5275 (2014).

Article CAS PubMed Google Scholar

Ma, R. et al. A review of oxygen reduction mechanisms for metal-free carbon-based electrocatalysts. npj Computat. Mater. 5(1), 1–15 (2019).

ADS Google Scholar

Gasteiger, H. A. et al. Activity benchmarks and requirements for Pt, Pt-alloy, and non-Pt oxygen reduction catalysts for PEMFCs. Appl. Catal. B 56(1–2), 9–35 (2005).

Article CAS Google Scholar

Guo, S. & Sun, S. FePt nanoparticles assembled on graphene as enhanced catalyst for oxygen reduction reaction. J. Am. Chem. Soc. 134(5), 2492–2495 (2012).

Article CAS PubMed Google Scholar

Jaouen, F. et al. Recent advances in non-precious metal catalysis for oxygen-reduction reaction in polymer electrolyte fuel cells. Energy Environ. Sci. 4(1), 114–130 (2011).

Article CAS Google Scholar

Xue, Y. et al. Transition metal oxide-based oxygen reduction reaction electrocatalysts for energy conversion systems with aqueous electrolytes. J. Mater. Chem. A 6(23), 10595–10626 (2018).

Article CAS Google Scholar

Jia, Q. et al. Metal and metal oxide interactions and their catalytic consequences for oxygen reduction reaction. J. Am. Chem. Soc. 139(23), 7893–7903 (2017).

Article CAS PubMed Google Scholar

Wang, Y., Li, J. & Wei, Z. Transition-metal-oxide-based catalysts for the oxygen reduction reaction. J. Mater. Chem. A 6(18), 8194–8209 (2018).

Article CAS Google Scholar

Gautam, J. et al. Mesoporous iron sulfide nanoparticles anchored graphene sheet as an efficient and durable catalyst for oxygen reduction reaction. J. Power Sources 427, 91–100 (2019).

Article ADS CAS Google Scholar

Xiao, J. et al. Raisin bread-like iron sulfides/nitrogen and sulfur dual-doped mesoporous graphitic carbon spheres: A promising electrocatalyst for the oxygen reduction reaction in alkaline and acidic media. J. Mater. Chem. A 5(22), 11114–11123 (2017).

Article CAS Google Scholar

Sun, K. et al. The oxygen reduction reaction rate of metallic nanoparticles during catalyzed oxidation. Sci. Rep. 7(1), 7017 (2017).

Article ADS PubMed PubMed Central Google Scholar

He, D. et al. Bifunctional effect of reduced graphene oxides to support active metal nanoparticles for oxygen reduction reaction and stability. J. Mater. Chem. 22(39), 21298–21304 (2012).

Article CAS Google Scholar

Antolini, E. Carbon supports for low-temperature fuel cell catalysts. Appl. Catal. B 88(1), 1–24 (2009).

Article CAS Google Scholar

Yang, G. & Park, S.-J. Conventional and microwave hydrothermal synthesis and application of functional materials: A review. Materials 12(7), 1177 (2019).

Article ADS CAS PubMed Central Google Scholar

Kumar, R. et al. Homogeneous reduced graphene oxide supported NiO-MnO2 ternary hybrids for electrode material with improved capacitive performance. Electrochim. Acta 303, 246–256 (2019).

Article CAS Google Scholar

Kumar, R. et al. Microwave heating time dependent synthesis of various dimensional graphene oxide supported hierarchical ZnO nanostructures and its photoluminescence studies. Mater. Des. 111, 291–300 (2016).

Article CAS Google Scholar

Kumar, R. et al. Facile and single step synthesis of three dimensional reduced graphene oxide-NiCoO2 composite using microwave for enhanced electron field emission properties. Appl. Surf. Sci. 416, 259–265 (2017).

Article ADS CAS Google Scholar

Kumar, R. et al. Nitrogen–sulfur co-doped reduced graphene oxide-nickel oxide nanoparticle composites for electromagnetic interference shielding. ACS Appl. Nanomater. 2(7), 4626–4636 (2019).

Article CAS Google Scholar

Kumar, R. et al. Graphene-wrapped and cobalt oxide-intercalated hybrid for extremely durable super-capacitor with ultrahigh energy and power densities. Carbon 79, 192–202 (2014).

Article CAS Google Scholar

Zhang, J. et al. Direct growth of flower-like manganese oxide on reduced graphene oxide towards efficient oxygen reduction reaction. Chem. Commun. 49(56), 6334–6336 (2013).

Article ADS CAS Google Scholar

Kumar, R. et al. Honeycomb-like open-edged reduced-graphene-oxide-enclosed transition metal oxides (NiO/Co3O4) as improved electrode materials for high-performance supercapacitor. J. Energy Storage 30, 101539 (2020).

Article Google Scholar

Kumar, R. et al. Microwave as a tool for synthesis of carbon-based electrodes for energy storage. ACS Appl. Mater. Interfaces. 14(18), 20306–20325 (2021).

Article PubMed Google Scholar

Kumar, R. et al. Microwave-assisted thin reduced graphene oxide-cobalt oxide nanoparticles as hybrids for electrode materials in supercapacitor. J. Energy Storage 40, 102724 (2021).

Article Google Scholar

Kumar, R. et al. A review on the current research on microwave processing techniques applied to graphene-based supercapacitor electrodes: An emerging approach beyond conventional heating. J. Energy Chem. 74, 252 (2022).

Article CAS Google Scholar

Yusoff, N. et al. A facile preparation of titanium dioxide-iron oxide@ silicon dioxide incorporated reduced graphene oxide nanohybrid for electrooxidation of methanol in alkaline medium. Electrochim. Acta 192, 167–176 (2016).

Article CAS Google Scholar

Shahabuddin, S. et al. Polyaniline-SrTiO3 nanocube based binary nanocomposite as highly stable electrode material for high performance supercapaterry. Ceram. Int. 45(9), 11428–11437 (2019).

Article CAS Google Scholar

Kumar, R. et al. An overview of recent progress in nanostructured carbon-based supercapacitor electrodes: From zero to bi-dimensional materials. Carbon 139, 298 (2022).

Article Google Scholar

Sun, M. et al. Graphene-based transition metal oxide nanocomposites for the oxygen reduction reaction. Nanoscale 7(4), 1250–1269 (2015).

Article ADS CAS PubMed Google Scholar

Garino, N. et al. Microwave-assisted synthesis of reduced graphene oxide/SnO2 nanocomposite for oxygen reduction reaction in microbial fuel cells. ACS Appl. Mater. Interfaces. 8(7), 4633–4643 (2016).

Article CAS PubMed Google Scholar

Zou, X., Wang, L. & Yakobson, B. I. Mechanisms of the oxygen reduction reaction on B-and/or N-doped carbon nanomaterials with curvature and edge effects. Nanoscale 10(3), 1129–1134 (2018).

Article CAS PubMed Google Scholar

Li, Y. et al. An oxygen reduction electrocatalyst based on carbon nanotube–graphene complexes. Nat. Nanotechnol. 7(6), 394–400 (2012).

Article ADS CAS PubMed Google Scholar

Guo, Y. et al. Hierarchical N-doped CNTs grafted onto MOF-derived porous carbon nanomaterials for efficient oxygen reduction. J. Colloid Interface Sci. 606, 1833–1841 (2022).

Article ADS CAS PubMed Google Scholar

Zhang, S. et al. Carbon nanotubes decorated with Pt nanoparticles via electrostatic self-assembly: A highly active oxygen reduction electrocatalyst. J. Mater. Chem. 20(14), 2826–2830 (2010).

Article CAS Google Scholar

Andersen, N. I., Serov, A. & Atanassov, P. Metal oxides/CNT nano-composite catalysts for oxygen reduction/oxygen evolution in alkaline media. Appl. Catal. B 163, 623–627 (2015).

Article CAS Google Scholar

Huang, N. M. et al. Simple room-temperature preparation of high-yield large-area graphene oxide. Int. J. Nanomed. 6, 3443 (2011).

Article CAS Google Scholar

Yao, Y. et al. Hydrothermal synthesis of Co3O4–graphene for heterogeneous activation of peroxymonosulfate for decomposition of phenol. Ind. Eng. Chem. Res. 51(46), 14958–14965 (2012).

Article CAS Google Scholar

Dong, Y. et al. A facile route to controlled synthesis of Co3O4 nanoparticles and their environmental catalytic properties. Nanotechnology 18(43), 435602 (2007).

Article Google Scholar

Shahid, M. M., Rameshkumar, P. & Huang, N. M. Morphology dependent electrocatalytic properties of hydrothermally synthesized cobalt oxide nanostructures. Ceram. Int. 41(10), 13210–13217 (2015).

Article CAS Google Scholar

Boucher, B., Buhl, R. & Perrin, M. Propriétés et structure magnétique de Mn3O4. J. Phys. Chem. Solids 32(10), 2429–2437 (1971).

Article ADS CAS Google Scholar

Laha, S., Mukherjee, R. & Lawes, G. Interactions and magnetic relaxation in boron doped Mn3O4 nanoparticles. Mater. Res. Express 1(2), 025032 (2014).

Article ADS CAS Google Scholar

Thakur, S. & Karak, N. Green reduction of graphene oxide by aqueous phytoextracts. Carbon 50(14), 5331–5339 (2012).

Article CAS Google Scholar

Hidayah, N., et al. Comparison on graphite, graphene oxide and reduced graphene oxide: Synthesis and characterization. In AIP Conference Proceedings. 2017. AIP Publishing LLC.

Dresselhaus, M. S. et al. Perspectives on carbon nanotubes and graphene Raman spectroscopy. Nano Lett. 10(3), 751–758 (2010).

Article ADS CAS PubMed Google Scholar

Low, F. W., Lai, C. W. & Abd Hamid, S. B. Easy preparation of ultrathin reduced graphene oxide sheets at a high stirring speed. Ceram. Int. 41(4), 5798–5806 (2015).

Article CAS Google Scholar

Stankovich, S. et al. Synthesis and exfoliation of isocyanate-treated graphene oxide nanoplatelets. Carbon 44(15), 3342–3347 (2006).

Article CAS Google Scholar

Larbi, T. et al. Nickel content effect on the microstructural, optical and electrical properties of p-type Mn3O4 sprayed thin films. J. Alloy. Compd. 626, 93–101 (2015).

Article CAS Google Scholar

Pan, N. et al. Removal of Th4+ ions from aqueous solutions by graphene oxide. J. Radioanal. Nucl. Chem. 298(3), 1999–2008 (2013).

Article CAS Google Scholar

Sunderrajan, S., Miranda, L. R. & Pennathur, G. Improved stability and catalytic activity of graphene oxide/chitosan hybrid beads loaded with porcine liver esterase. Prep. Biochem. Biotechnol. 48(4), 343–351 (2018).

Article CAS PubMed Google Scholar

Raha, S., Mohanta, D. & Ahmaruzzaman, M. Novel CuO/Mn3O4/ZnO nanocomposite with superior photocatalytic activity for removal of Rabeprazole from water. Sci. Rep. 11(1), 1–19 (2021).

Article Google Scholar

Mohamed, M. M. & El-Farsy, H. Rapid reduction of nitroarenes photocatalyzed by an innovative Mn3O4/α-Ag2WO4 nanoparticles. Sci. Rep. 10(1), 1–18 (2020).

Article CAS Google Scholar

Guo, H.-L. et al. A green approach to the synthesis of graphene nanosheets. ACS Nano 3(9), 2653–2659 (2009).

Article CAS PubMed Google Scholar

Gurbuz, F., Ciftci, H. & Akcil, A. Biodegradation of cyanide containing effluents by Scenedesmus obliquus. J. Hazard. Mater. 162(1), 74–79 (2009).

Article CAS PubMed Google Scholar

Ameer, S. & Gul, I. H. Influence of reduced graphene oxide on effective absorption bandwidth shift of hybrid absorbers. PLoS ONE 11(6), e0153544 (2016).

Article PubMed PubMed Central Google Scholar

Jana, M. et al. Bio-reduction of graphene oxide using drained water from soaked mung beans (Phaseolus aureus L.) and its application as energy storage electrode material. Mater. Sci. Eng.: B 186, 33–40 (2014).

Article CAS Google Scholar

Shahabuddin, S. et al. Synthesis of chitosan grafted-polyaniline/Co3O4 nanocube nanocomposites and their photocatalytic activity toward methylene blue dye degradation. RSC Adv. 5(102), 83857–83867 (2015).

Article ADS CAS Google Scholar

Zhang, H., Hines, D. & Akins, D. L. Synthesis of a nanocomposite composed of reduced graphene oxide and gold nanoparticles. Dalton Trans. 43(6), 2670–2675 (2014).

Article CAS PubMed Google Scholar

Ahmed, K. A. M. & Huang, K. Formation of Mn3O4 nanobelts through the solvothermal process and their photocatalytic property. Arab. J. Chem. 12(3), 429–439 (2019).

Article CAS Google Scholar

Atique Ullah, A. et al. Oxidative degradation of methylene blue using Mn3O4 nanoparticles. Water Conserv. Sci. Eng. 1(4), 249–256 (2017).

Article Google Scholar

Jia, J. et al. A method to construct a third-generation horseradish peroxidase biosensor: Self-assembling gold nanoparticles to three-dimensional sol− gel network. Anal. Chem. 74(9), 2217–2223 (2002).

Article CAS PubMed Google Scholar

Omar, F. S. et al. Effect of physical interaction between polyaniline and metal phosphate nanocomposite as positive electrode for supercapattery. J. Energy Storage 32, 101850 (2020).

Article Google Scholar

Muhammad, S. et al. Understanding the basics of electron transfer and cyclic voltammetry of potassium ferricyanide-an outer sphere heterogeneous electrode reaction. J. Chem. Soc. Pak. 42(6), 813 (2020).

CAS Google Scholar

Cheah, M. H. & Chernev, P. Electrochemical oxidation of ferricyanide. Sci. Rep. 11(1), 23058 (2021).

Article ADS CAS PubMed PubMed Central Google Scholar

Choi, W. et al. Modeling and applications of electrochemical impedance spectroscopy (EIS) for lithium-ion batteries. J. Electrochem. Sci. Technol. 11(1), 1–13 (2020).

Article CAS Google Scholar

Matemadombo, F. & Nyokong, T. Characterization of self-assembled monolayers of iron and cobalt octaalkylthiosubstituted phthalocyanines and their use in nitrite electrocatalytic oxidation. Electrochim. Acta 52(24), 6856–6864 (2007).

Article CAS Google Scholar

Liang, Y. et al. Co3O4 nanocrystals on graphene as a synergistic catalyst for oxygen reduction reaction. Nat. Mater. 10(10), 780–786 (2011).

Article ADS CAS PubMed Google Scholar

Shahid, M. M. et al. A cobalt oxide nanocubes interleaved reduced graphene oxide nanocomposite modified glassy carbon electrode for amperometric detection of serotonin. Mater. Sci. Eng. C 100, 388–395 (2019).

Article CAS Google Scholar

Shahid, M. M. et al. An electrochemical sensing platform based on a reduced graphene oxide–cobalt oxide nanocube@ platinum nanocomposite for nitric oxide detection. J. Mater. Chem. A 3(27), 14458–14468 (2015).

Article CAS Google Scholar

Choe, J. E. et al. Manganese dioxide/reduced graphene oxide with poly (3, 4-ethylenedioxythiophene) for improved electrocatalytic oxygen reduction reaction. J. Nanosci. Nanotechnol. 15(8), 5684–5690 (2015).

Article CAS PubMed Google Scholar

Lee, K., Ahmed, M. S. & Jeon, S. Electrochemical deposition of silver on manganese dioxide coated reduced graphene oxide for enhanced oxygen reduction reaction. J. Power Sources 288, 261–269 (2015).

Article ADS CAS Google Scholar

Qian, Y., Lu, S. & Gao, F. Synthesis of manganese dioxide/reduced graphene oxide composites with excellent electrocatalytic activity toward reduction of oxygen. Mater. Lett. 65(1), 56–58 (2011).

Article CAS Google Scholar

Su, Y. et al. High-performance manganese nanoparticles on reduced graphene oxide for oxygen reduction reaction. Catal. Lett. 146(6), 1019–1026 (2016).

Article CAS Google Scholar

Jha, P. K. et al. In-situ generated Mn3O4-reduced graphene oxide nanocomposite for oxygen reduction reaction and isolated reduced graphene oxide for supercapacitor applications. Carbon 154, 285–291 (2019).

Article CAS Google Scholar

Zhang, Y. et al. One-step synthesis of an octahedral Mn3O4/rGO composite for use as an electrocatalyst in the oxygen reduction reaction. J. Solid State Electrochem. 22(7), 2159–2168 (2018).

Article CAS Google Scholar

Rameshkumar, P., Praveen, R. & Ramaraj, R. Electroanalysis of oxygen reduction and formic acid oxidation using reduced graphene oxide/gold nanostructures modified electrode. J. Electroanal. Chem. 754, 118–124 (2015).

Article CAS Google Scholar

Chai, H. et al. Facile synthesis of Mn3O4-rGO hybrid materials for the high-performance electrocatalytic reduction of oxygen. J. Colloid Interface Sci. 488, 251–257 (2017).

Article ADS CAS PubMed Google Scholar

Zheng, Y. et al. Nanostructured metal-free electrochemical catalysts for highly efficient oxygen reduction. Small 8(23), 3550–3566 (2012).

Article CAS PubMed Google Scholar

Lu, X. et al. Interconnected core–shell carbon nanotube–graphene nanoribbon scaffolds for anchoring cobalt oxides as bifunctional electrocatalysts for oxygen evolution and reduction. J. Mater. Chem. A 3(25), 13371–13376 (2015).

Article CAS Google Scholar

Download references

This study was supported by Thammasat Postdoctoral Fellowship and the NSRF via the Program Management Unit for Human Resources & Institutional Development, Research and Innovation [grant number B16F640084]. The authors gratefully acknowledged support from the Center of Excellence in Materials and Plasma Technology (CoE M@P Tech), Thammasat University, Thailand.

School of Integrated Science and Innovation (ISI), Sirindhorn International Institute of Technology (SIIT), Thammasat University, Rangsit, 12121, Pathum Thani, Thailand

Mehmood Shahid, Thilina Rajeendre Katugampalage, Chariya Kaewsaneha, Paiboon Sreearunothai & Pakorn Opaprakasit

Graphene and Advanced 2D Materials Research Group (GAMRG), School of Engineering and Technology, Sunway University, No. 5, Jalan Universiti, Bandar Sunway, 47500, Subang Jaya, Selangor, Malaysia

Mohammad Khalid

Malaysia – Japan International Institute of Technology (MJIIT), Universiti Teknologi Malaysia, Jalan Sultan Yahya Petra, 54100, Kuala Lumpur, Malaysia

Waqar Ahmed

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

The project was designed, executed, and the nanocomposite was synthesized by Shahid Mehmood. The manuscript was written by Shahid Mehmood as well. Thilina Rajeendre Katugampalage contributed to the interpretation of XRD and in the preparation of the graphical abstract. Mohammad Khalid and Waqar Ahmed were involved in modifying and enhancing the writing of UV-vis and FTIR studies. Chariya Kaewsaneha, Paiboon Sreearunothai, and Pakorn Opaprakasit have edited and enhanced the writing style of the whole manuscript.

Correspondence to Mehmood Shahid, Chariya Kaewsaneha or Pakorn Opaprakasit.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Shahid, M., Katugampalage, T.R., Khalid, M. et al. Microwave assisted synthesis of Mn3O4 nanograins intercalated into reduced graphene oxide layers as cathode material for alternative clean power generation energy device. Sci Rep 12, 19043 (2022). https://doi.org/10.1038/s41598-022-23622-x

Download citation

Received: 30 July 2022

Accepted: 02 November 2022

Published: 09 November 2022

DOI: https://doi.org/10.1038/s41598-022-23622-x

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

SHARE