A one

Scientific Reports volume 12, Article number: 16537 (2022) Cite this article

591 Accesses

1 Altmetric

Metrics details

This is a brief report on the fabrication of concentric multi-element metallic carpets through a one-pot rotational bipolar electro-engineering procedure. A suspended piece of nickel foam as a bipolar electrode (BPE) is rotated in an aqueous solution containing a ternary mixture of metal ions when sufficient DC potential is applied to driving electrodes. The customizable tools of this art are potential gradient, rotation, and concentration/kinetic polarizations. Creating the multi-element radial gradient is typically tested in a one-pot artistic jewelry electroplating.

One-pot electrodeposition (electroplating) is a facile approach for the deposition of dissolved electroactive ionic species, specifically metal ions, on conductive substrates for the fabrication of various types of two-/three-dimensional materials coatings1,2,3. One of the limitations of electroplating is the impossibility of creating gradients of materials (isolated material zones) perpendicular to the applied field, which arises from the uniformity of the applied potential across the working electrode in conventional electrochemistry.

Bipolar electrochemistry (BE) affords a potential gradient across the bipolar electrodes (BPE) immersed in electrolytes with no direct electrical connection. The applied interfacial potential difference drives redox reactions on extremities (poles) of BPE. The upgraded forms of this ability in the electrolyte containing electroactive metal ions with a stationary floating conductor will be useful in wireless electroplating4,5,6,7,8,9,10,11,12,13,14. Upon implementing a sufficient DC potential to driving electrodes, due to the creation of a potential drop across the driving electrodes, a linearly decreasing potential difference between the extremities of the suspended object is generated that drives opposite redox reactions at both sides of BPE15,16,17,18.

The major drawback in the already bipolar electroplating studies19,20,21,22,23,24,25,26,27,28,29,30,31 is the impossibility of the intermittent change of the bipolar cathode/anode position thus the electrodeposition only occurs at one pole of the BPE. To this end, a spatiotemporal polarity change of the anode/cathode poles32,33,34 can be attained through an AC power supply to implement an alternating potential to the driving electrodes. Over the last decade, some research works explored the control motion of wireless conducting objects to enable different types of self-propulsion35,36,37,38,39. A more exhaustive and customizable approach that permits applying the interfacial gradient potential to the entire 360° of BPE margin is the rotation of BPE using a motor controller and a DC power supply. It allows applying a uniform, successive and consistent potential gradient throughout BPE. The electroplated composite prepared by this method delivers a concentric multi-element composition of the isolated metal alloys40.

In this work, the adjustment of bipolar gradient potential as a function of applied DC potential, the rotation speed of BPE, inherent kinetic polarization of the metal ions (standard reduction potentials) and concentration polarization (concentration of precursors) generate a combinational gradient potential sensed by the rotated-BPE, endowing a concentric isolated alloy across the center-to-borders of BPEs. We exploited this methodology in an artistic one-pot electro-engineering of two typical ternary mixtures of Cu-Ni-Mn and Cu-Co-Mn at nickel foam (NF) as the bipolar electrode.

A two-dimensional carpet-resemble isolated concentric metallic zones of Cu-Ni-Mn are typically prepared through rotational DC-bipolar electroplating. A constant DC potential (from 4 to 12 V) was applied between a pair of stainless-steel driving electrodes with a separation distance of ca. 2.5 cm, as the length of the bipolar cell. One piece of NF (10 × 12 mm) as a typical BPE was connected to the shaft of a motor controller, immersed in the middle of the BP cell containing a particular solution of the metal ions, and was rotated at a constant speed of 100 rpm (further information on the experimental section is in SI). Figure S1 discloses the place of attachment of BPE to the rotator tip that remained unchanged (the upper side is designated in Fig. S1). Since the concentric gradients formed at both sides of BPE are symmetrical, this issue can be resolved by exchange of the attachment place from one side to the other side of BPE at half-time of electroplating. Considering the existence of a potential gradient from the edge to the center of BPE, selecting variable concentrations of the electroactive metal ions with different standard reduction potentials allows the control of kinetic and concentration polarizations to control the fabricated fade concentric gradient across the BPE. Moreover, the polarity changes through rotation allowing the one-pot electro-engineering of the metallic carpet. Before anything, we aimed to explore the actual role of anodic and cathodic poles of BPE on electroplating and electrodissolution of the metallic layers. To this end, a facile static bipolar electroplating was accomplished to distinguish the role of the anode and cathode of BPE in the formation of metallic carpets. The linear metallic gradient was just formed at the cathodic side, as shown in Fig. S2. The possible anodic dissolution of deposited layers at cathodic layers was also studied through static electroplating (at 8 V) of metal ions separately on three distinct nickel foam (Fig. S3). After cathodic electroplating, the position of bipolar poles was exchanged through 180° rotation of BPE to consider possible dissolution of the electroplated layers. For the Cu layer, after rotation, the primary deposited layer on edge of BPE dissolved at the anodic potential (see Fig. S3). In the case of Ni, the dissolution was lower, while for the Mn, the deposited cathodic layer did not change, confirming a gradual diminishing trend of Cu > Ni >  > Mn. This relative trend is determinant along the rotational electroplating of Cu, Ni and Mn.

One of the main discriminators is the maximum potential sensed by the extremities of the BPE, in which the electroactive species with high reduction potentials (Mn) can be easily deposited just on the edges of the negatively charged BPE (during the cathodic half-cycle of the rotating BPE)1, as well as, the anodic dissolution of Cu and Ni that intensifies the isolation of the individual metallic zones. The overpotential along the BE gradually reduces by moving toward the center of BPE thus the cations with lower-reduction overpotentials (like Ni2+ and Cu2+) can deposit at the middle and center of the BPE, respectively (as shown in Fig. 1a). The rotation of the rectangular BPE around a central axis between the driving electrodes leads to AC-bipolar electrochemistry (Fig. 1b). The polarity change originated from the 360° rotation affords a uniform concentric gradient along all four sides of the BPE, enabling electroplating of the isolated metallic zones in an ellipse-like form. To illustrate an in-depth picture of the changes, the rotational speed was practically slowed down through a four manual rotation-section 90° of the bipolar electrode (Fig. 1c). The equivalent photographic image of this schematic is presented as Fig. 1d. The longitudinal faces (X1 and X2) and transverse faces (Y1 and Y2) are marked in Fig. 1a. By implementing the first reducing gradient potential on Y1, the first linear metal composing was attained. Upon rotation from 0 ͦ to 90 ͦ, the Y1 face is replaced by X1 and, thus, a cross-sectional ternary (e.g., Cu, Ni and Mn) electrodeposition can be formed. In the same way, the rotation of the different faces of BPE through rotation degrees of 180 ͦ, 270 ͦ and 360 ͦ make possible the formation of triple intersecting gradients. The photographic images inserted in Fig. 1c show a rectangle radiant of the metallic zone with sharp corners. Meanwhile, the minimum rotation rate of 100 rpm provides ellipse-like concentric metallic zones.

(a) Potential distribution within the BPE. (b) Schematic presentation of the set-up used for the bipolar electrodeposition of Cu–Ni–Mn gradients. The formed concentric pattern are identical on both sides of BPE, although, a centric place of rotor attachment remained unchanged at the upper face of nickel foam, see Fig. S1). (c) Schematic presentation of dependency of electrodeposition on the BPE orientation. (d) The photograph was taken from four manual rotations of the BPE (90° to 360°).

The potential-difference across the BPE (ΔEBPE) drops linearly along BPE as a fraction of Etot. It can be directly estimated from the Eq. (1)17:

Here, Etot is the externally applied potential between the two driving electrodes, LBPE is the length of BPE (bare NF), and Lchannel the distance between the driving electrodes (stainless steel plates).

We first applied a non-optimized potential of 4 V as the minimum operating potential to the driving electrodes for a specific time. The optical images and corresponding elemental mappings based on energy-dispersive X-ray spectroscopy were taken from NF electrodes to disclose how to arrange the created metallic carpet array on the NF-BPE surface. The equivalent EDX spectrum is presented in Fig. S4. The results show improper isolation on the metallic zones created at 4 V (Fig. 2). At such a low overpotential of 4 V, Cu is the predominant form deposited throughout the central region to near the margins, and, Ni is more likely to deposit on the edges, while the visual inspection shows no Mn deposition, and low anodic dissolution of the electroplated Cu layer (a bimetallic carpet forms).

The optical and equivalent mapping analyses taken from metallic carpet formed by applying a potential of 4 V at rotating rate of 100 rpm, concentration of Cu, Ni and Mn nitrates in bipolar cell were 0.02,0.2 and 0.4 M, respectively. The corresponding EDX spectrum are in Fig. S4.

The ternary metallic carpets of Cu, Ni and Mn are obtained at higher applied DC-potentials, as big as 8 V. By increasing the potential from 4 V, the Mn deposition increases, and it is completely observable at 8 V (Fig. 3). The results of mapping analyses demonstrate a uniform pattern of oxygen throughout the BPE, indicating an appealing-colored combination of the metal-oxides. The formation of oxides was typically shows in mapping analysis and approved by EDX spectrum shown in Fig. S5. Due to the positive standard reduction potential, it is expected copper covers the entire NFBPE. Nevertheless, the manipulation of ion concentration and the applied potentials permit confining the effect of standard potentials to achieve a one-pot compositional gradient.

The optical and equivalent mapping analyses taken from the metallic carpet of Cu, Ni and Mn formed by applying a driving potential of 8 V. The corresponding EDX spectrum is shown in Fig. S5.

The effect of the applied potential was studied on the fabrication of the metallic carpets at the different dc potentials of 4, 8 and 12 V. The optical images and the corresponding mapping analyses are compared in Fig. 4 to unravel the possible deposition at each zone, elemental patterning and the zone expansion (isolation). As shown in Fig. 4a, at 4 V, no observable manganese was deposited. While the edges of BPE are entirely occupied by Ni, confirming a sufficient potential for Ni reduction at the borders and insufficient for the Mn deposition. Further, upon the increase of potential to 8 V, Mn replaces Ni and deposits at the margin of BPE. At 12 V, the amount of the deposited Mn increases and expands toward the middle zone, such a behavior observes for the electroplated Ni, too. In all these cases, the Cu zone is restricted to the center of BPE with minimal changes, although, upon increasing potential, it gets a smaller diameter, which could be justified by the increase of the absolute value of the anodic potential toward the center of BPE (see Fig. 4a). Indeed, the rotation of NF will expose the Cu-zone to greater positive potentials and the siege ring of the positive potential at anodic half-cycle becomes tighter and tighter as the DC potential increases. The visual inspection of NF indicates the formation of exclusive metallic carpet engineered at each potential over the entire studied potential range of 4 to 12 V, however, the more isolated metallic carpets were obtained at 8 V compared to 4 and 12 V.

The optical and equivalent mapping analyses taken from metallic carpets formed at (a) different applied potentials and (b) different sets of metallic ions concentration.

The effect of concentration polarization was investigated on the expansion of the isolated zones and thermodynamics of deposition, which allows the altering net potential sensed by BPE and customizing the compositional gradient, as shown in Fig. 4b. The mapping images show possible controlled isolation of the Mn zone by concentration. In the case of the Cu zone, keeping concentration constant leads to a repeatable zone formed at different runs. The increase in the concentration of Ni(NO3)2 (from 0.2 to 0.4 M) shows an increase in the deposition and relative expansion of the Ni zone. Similar behavior was observed upon increasing the concentration of Mn(NO3)2 from 0.2 to 0.4 M. The established method was also tested for isolating Cu, Co and Mn as a new metallic carpet on nickel foam. As shown in Fig. 5, the satisfactory results are confirmed by optical image, the respective elemental mapping analysis, and the EDX spectra (see Fig. S7), which approve the possibility of the rotational BPE for the further combination of metallic carpets aiming for different propositions.

Mapping result of the Cu–Co–Mn metallic carpet formed by applying a potential of 8 V. The equivalent EDX spectra are presented in Fig. S7.

The use of metal nitrate salts at neutral pH allows base generation and precipitation of metal oxides41. It seems that in the center of BPE, the Cu(II) ions reduce to Cu(I) and, subsequently, react with water to form a red-colored Cu2O42. Since the oxidation condition of Cu2O to CuO at the anodic half cycle is not provided around the central zone, the color does not change to black CuO. It is well known that Cu2O is not stable against corrosion at positive potentials in neutral pHs43. This is the main reason for the anodic dissolution of the Cu layer at the middle and border zones. Therefore, at high positive potentials of the anodic half-cycles, the electroplated Cu is restricted to the central zones, especially in higher DC potentials, as shown in Fig. 4a. Since the pH of electrolyte is not acidic, the anodic deposition of MnO2 does not occur, and it was assumed to be cathodically deposited as MnO44,45, as the static bipolar electroplating shows no observable Mn deposition during the anodic cylce.

To further confirm the in situ production of hydroxide anions, we conducted a blank BP experiment in the cell containing a solution of 1.2 M of KNO3 + 20 µl of phenolphthalein (PhP) indicator (the value of 1.2 M is equal to the total nitrate concentration resulting from three metal salts of Cu(NO3)2 = 0.02 M, Ni(NO3)2 = 0.2 and Mn(NO3)2 = 0.4 M). The colorless potassium nitrate-PhP solution was chosen so that we could easily observe the color change. A DC potential of 8 V was applied to the floated NF through the stainless steel driving electrodes. Upon turning on the power supply, the color of the local solution of the anodic poles of the driving and bipolar electrodes immediately changed to pink color, indicating the generation of the hydroxide ions via electroreduction of nitrate ions (Fig. S6). A similar experiment in the solution of colored transition metal salts, but due to the deep color of the environment, the resulting red color is not clear. On this basis, and based on the EDX spectrums (Figs. S4 and S5) that confirmed the presence of oxygen, we propose a well-known overall electrochemical reaction pathway as below46:

From a physical point of view, it seems that other equivalent physical occurrences can be effective in emerging these ring patterns. Upon the rotation of the BPE, as a conductor current flows through it, a magnetic field creates perpendicular to the current. This event causes a potential difference transverse to current flow in the electrical conductor (BPE), known as Hall voltage. The superposition of this potential on the already cell voltage can induce some nonlinearity in the potential of BPE. Hall voltage as a key factor can play a latent role in controlling the ring pattern and distributing charge species. In parallel, in the presence of a magnetic field, the charged species experience a force called the Lorentz force47,48. Without this magnetic field, the charges follow an approximate behavior in a straight path. While, upon applying a perpendicular magnetic field, their paths between collisions are curved and, thus, the moving charges accumulate on one face of the material. These fundamental challenges can become a subject for future studies of the effects involved in the formation of these concentric gradients. Further application of this procedure was tested for future jewelry, as shown in Fig. 6.

One-pot carpet-like bipolar electro-engineering used in future jewelry.

We perused the effect of higher rotating rates of 200, 300, 400, 600, 800, 1000, and 1200 rpm to gain additional information on the rotational electroplating of Cu, Ni, and Mn. The as-prepared carpets are shown in Fig. S8, where in all rotation rates, the concentric gradients were obtained, however, with the increase in rotation speed, some changes are obvious. The images show a gradual narrowing in Mn-margin upon increasing rotation rate, while the central copper zone does not change significantly. Along with the retreating of manganese, nickel expands to the edges of BPE. It is hypothesized that in parallel with the increase of rotation rates and switching frequency of the BPE poles, Mn deposition reaction with a relatively slower kinetic lagged behind the reduction reaction of Ni and Cu.

This work discussed the preliminary studies performed on a new one-pot electro-engineering approach for the formation of two typical carpet-like ternary composites of Cu–Ni–Mn and Cu–Co–Mn at NFBPE. The effect of different physical parameters like DC potential, concentration polarization, kinetic polarizations, and rotation speed has been investigated to strongly support the observed changes in the pattern of metallic carpets. The results dedicated some exclusive features including, the one-pot formation of the wireless isolated concentric metallic composites, the simultaneous controlling of all zones of the compositional gradient, the ability to fabricate symmetrical composites on mobile electrodes in the electrolyte, and the creation of the compositional gradient over the surface of an electrode for future applications in artistic jewelry, nanomotor construction and so on. An ambitious goal of this idea is its future use as a cornerstone in materials engineering for multiple applications such as the design of new nanomotors, jewelry, electrochemical mechanistic studies, etc.

The datasets used and/or analysed during the current study available from the corresponding author on reasonable request.

Termebaf, H., Shayan, M. & Kiani, A. Two-step bipolar electrochemistry: Generation of composition gradient and visual screening of electrocatalytic activity. Langmuir 31, 13238–13246 (2015).

Article CAS PubMed Google Scholar

Xu, F. et al. One-step deposition of NixCu1−x alloys with both composition gradient and morphology evolution by bipolar electrochemistry. J. Electroanal. Chem. 823, 213–220 (2018).

Article CAS Google Scholar

Tisserant, G. et al. Generation of metal composition gradients by means of bipolar electrodeposition. Electrochim. Acta 179, 276–281 (2015).

Article CAS Google Scholar

Lundgren, A., Munktell, S., Lacey, M., Berglin, M. & Björefors, F. Formation of gold nanoparticle size and density gradients via bipolar electrochemistry. ChemElectroChem 3, 378–382 (2016).

Article CAS Google Scholar

Kayran, Y. U., Eßmann, V., Grützke, S. & Schuhmann, W. Selection of highly SERS-active nanostructures from a size gradient of Au nanovoids on a single bipolar electrode. ChemElectroChem 3, 399–403 (2016).

Article CAS Google Scholar

Loget, G., So, S., Hahn, R. & Schmuki, P. Bipolar anodization enables the fabrication of controlled arrays of TiO2 nanotube gradients. J. Mater. Chem. A 2, 17740–17745 (2014).

Article CAS Google Scholar

Jia, Q. et al. Electronic conductive and corrosion mechanisms of dual nanostructure CuCr-doped hydrogenated carbon films for SS316L bipolar plates. Mater. Today Chem. 21, 100521 (2021).

Article CAS Google Scholar

Ishiguro, Y., Inagi, S. & Fuchigami, T. Gradient doping of conducting polymer films by means of bipolar electrochemistry. Langmuir 27, 7158–7162 (2011).

Article CAS PubMed Google Scholar

Inagi, S. Fabrication of gradient polymer surfaces using bipolar electrochemistry. Polym. J. 48, 39–44 (2016).

Article CAS Google Scholar

Qin, C. et al. Bipolar electroactive conducting polymers for wireless cell stimulation. Appl. Mater. Today 21, 100804 (2020).

Article Google Scholar

Malytska, I., Doneux, T., Bougouma, M., Kuhn, A. & Bouffier, L. Wireless addressing of freestanding MoSe2 macro- and microparticles by bipolar electrochemistry. J. Phys. Chem. C 123, 5647–5652 (2019).

Article CAS Google Scholar

Tan, S. M. & Pumera, M. Composition-graded MoWSx hybrids with tailored catalytic activity by bipolar electrochemistry. ACS Appl. Mater. Interfaces 9, 41955–41964 (2017).

Article CAS PubMed Google Scholar

Wang, H. et al. Development of a bipolar electrochemical flow microreactor for recovery of valuable metals from mixed solutions. Chem. Eng. J. 382, 121907 (2020).

Article CAS Google Scholar

Sequeira, C. A. C., Cardoso, D. S. P. & Gameiro, M. L. F. Bipolar electrochemistry, a focal point of future research. Chem. Eng. Commun. 203, 1001–1008 (2016).

Article CAS Google Scholar

Mavré, F. et al. Bipolar electrodes: A useful tool for concentration, separation, and detection of analytes in microelectrochemical systems. Anal. Chem. 82, 8766–8774 (2010).

Article PubMed Google Scholar

Fosdick, S. E., Knust, K. N., Scida, K. & Crooks, R. M. Bipolar electrochemistry. Angew. Chem. Int. Ed. 52, 10438–10456 (2013).

Article CAS Google Scholar

Loget, G. & Kuhn, A. Bipolar electrochemistry in the nanosciences. in Electrochemistry: Nanosystems Electrochemistry (Wadhawan J., Compton R., eds.). Vol. 11. 71–103 (RSC Publishing, 2012).

Sun, Z. et al. Creating a bipolar electrode system for electrochemical advanced oxidative processes with efficient electricity consumption. J. Environ. Chem. Eng. 9, 105694 (2021).

Article CAS Google Scholar

Ismail, A. et al. Enhanced bipolar electrochemistry at solid-state micropores: Demonstration by wireless electrochemiluminescence imaging. Anal. Chem. https://doi.org/10.1021/acs.analchem.9b00559 (2019).

Article PubMed Google Scholar

Gamero-Quijano, A., Molina-Osorio, A. F., Peljo, P. & Scanlon, M. D. Closed bipolar electrochemistry in a four-electrode configuration. Phys. Chem. Chem. Phys. 21, 9627–9640 (2019).

Article CAS PubMed Google Scholar

Gholami, F. et al. Direct enzymatic glucose/O2 biofuel cell based on poly-thiophene carboxylic acid alongside gold nanostructures substrates derived through bipolar electrochemistry. Sci. Rep. 8, 1–14 (2018).

Article Google Scholar

Wang, Y., Mayorga-Martinez, C. C., Chia, X., Sofer, Z. & Pumera, M. Nonconductive layered hexagonal boron nitride exfoliation by bipolar electrochemistry. Nanoscale 10, 7298–7303 (2018).

Article CAS PubMed Google Scholar

Mazánek, V., Mayorga-Martinez, C. C., Bouša, D., Sofer, Z. & Pumera, M. WSe2 nanoparticles with enhanced hydrogen evolution reaction prepared by bipolar electrochemistry: Application in competitive magneto-immunoassay. Nanoscale 10, 23149–23156 (2018).

Article PubMed Google Scholar

Patterson, N. & Ignaszak, A. Modification of glassy carbon with polypyrrole through an aminophenyl linker to create supercapacitive materials using bipolar electrochemistry. Electrochem. commun. 93, 10–14 (2018).

Article CAS Google Scholar

Malytska, I. et al. Bipolar electrochemistry with organic single crystals for wireless synthesis of metal-organic Janus objects and asymmetric photovoltage generation. J. Phys. Chem. C 121, 12921–12927 (2017).

Article CAS Google Scholar

Crouch, G. M., Han, D., Fullerton-Shirey, S. K., Go, D. B. & Bohn, P. W. Addressable direct-write nanoscale filament formation and dissolution by nanoparticle-mediated bipolar electrochemistry. ACS Nano 11, 4976–4984 (2017).

Article CAS PubMed PubMed Central Google Scholar

Jiang, J. Z., Guo, M. H., Yao, F. Z., Li, J. & Sun, J. J. Propulsion of copper microswimmers in folded fluid channels by bipolar electrochemistry. RSC Adv. 7, 6297–6302 (2017).

Article CAS ADS Google Scholar

Chow, K. F., Mavré, F. & Crooks, R. M. Wireless electrochemical DNA microarray sensor. J. Am. Chem. Soc. 130, 7544–7545 (2008).

Article CAS PubMed Google Scholar

Dorri, N., Shahbazi, P. & Kiani, A. Self-movement of water droplet at the gradient nanostructure of cu fabricated using bipolar electrochemistry. Langmuir 30, 1376–1382 (2014).

Article CAS PubMed Google Scholar

Khoshfetrat, S. M., Ranjbari, M., Shayan, M., Mehrgardi, M. A. & Kiani, A. Wireless electrochemiluminescence bipolar electrode array for visualized genotyping of single nucleotide polymorphism. Anal. Chem. 87, 8123–8131 (2015).

Article CAS PubMed Google Scholar

Koizumi, Y., Nishiyama, H., Tomita, I. & Inagi, S. Templated bipolar electrolysis for fabrication of robust Co and Pt nanorods. Chem. Commun. 54, 10475–10478 (2018).

Article CAS Google Scholar

Koizumi, Y. et al. Electropolymerization on wireless electrodes towards conducting polymer microfibre networks. Nat. Commun. 7, 1–6 (2016).

Article Google Scholar

Watanabe, T. et al. In-plane growth of poly(3,4-ethylenedioxythiophene) films on a substrate surface by bipolar electropolymerization. ACS Macro Lett. 7, 551–555 (2018).

Article CAS PubMed Google Scholar

Asoh, H., Miura, S. & Hashimoto, H. One-pot synthesis of Pt/alumina composites via AC-bipolar electrochemistry. ACS Appl. Nano Mater. 2, 1791–1795 (2019).

Article CAS Google Scholar

Eßmann, V. et al. Wireless light-emitting electrochemical rotors. J. Phys. Chem. Lett. 8, 4930–4934 (2017).

Article PubMed Google Scholar

Dauphin, A. L. et al. Tracking magnetic rotating objects by bipolar electrochemiluminescence. J. Phys. Chem. Lett. 10, 5318–5324 (2019).

Article CAS PubMed Google Scholar

Dauphin, A. L., Arbault, S., Kuhn, A., Sojic, N. & Bouffier, L. Remote actuation of a light-emitting device based on magnetic stirring and wireless electrochemistry. ChemPhysChem 21, 600–604 (2020).

Article CAS PubMed Google Scholar

Loget, G. & Kuhn, A. Electric field-induced chemical locomotion of conducting objects. Nat. Commun. 2, 1–6 (2011).

Article Google Scholar

Salinas, G. et al. Asymmetry controlled dynamic behavior of autonomous chemiluminescent Janus microswimmers. Chem. Sci. 11, 7438–7443 (2020).

Article CAS PubMed PubMed Central Google Scholar

Eßmann, V., Clausmeyer, J. & Schuhmann, W. Alternating current-bipolar electrochemistry. Electrochem. Commun. 75, 82–85 (2017).

Article Google Scholar

Li, J. & Zhitomirsky, I. Cathodic electrophoretic deposition of manganese dioxide films. Colloids Surfaces A Physicochem. Eng. Asp. 348, 248–253 (2009).

Article CAS Google Scholar

Yang, Y. et al. Controllable morphology and conductivity of electrodeposited Cu2O thin film: Effect of surfactants. ACS Appl. Mater. Interfaces 6, 22534–22543 (2014).

Article CAS PubMed Google Scholar

Thompson, W. T., Kaye, M. H., Bale, C. W. & Pelton, A. D. Pourbaix diagrams for multielement systems. Uhlig's Corrosion Handb. 3, 103–109 (2011).

Article Google Scholar

Hunter, B. M., Gray, H. B. & Müller, A. M. Earth-abundant heterogeneous water oxidation catalysts. Chem. Rev. 116, 14120–14136 (2016).

Article CAS PubMed Google Scholar

Pourbaix, M., Zhang, H. & Pourbaix, A. Presentation of an Atlas of chemical and electrochemical equilibria in the presence of a gaseous phase. Mater. Sci. Forum 251–254, 143–148 (1997).

Article Google Scholar

Yan, Z. et al. Anion insertion enhanced electrodeposition of robust metal hydroxide/oxide electrodes for oxygen evolution. Nat. Commun. 9, 1–9 (2018).

Article ADS Google Scholar

Hall, E. H. On a new action of the magnet on electric currents. Am. J. Math. 2, 287–292 (1879).

Article MathSciNet MATH Google Scholar

Sinova, J., Valenzuela, S. O., Wunderlich, J., Back, C. H. & Jungwirth, T. Spin hall effects. Rev. Mod. Phys. 87, 1213–1260 (2015).

Article ADS Google Scholar

Download references

Department of Chemistry, Razi University, Kermanshah, Iran

Fereshte Gholami, Mojtaba Shamsipur & Afshin Pashabadi

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

F.G. performed all experimental studies and characterizations. A.P. wrote the main framework of the manuscript and scientific interprations. M.S. supports scientifically all contributions and finally reviewed the manuscript. All authors reviewed the manuscript.

Correspondence to Mojtaba Shamsipur or Afshin Pashabadi.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Gholami, F., Shamsipur, M. & Pashabadi, A. A one-pot rotational DC-bipolar approach for fabricating artistic metallic carpets. Sci Rep 12, 16537 (2022). https://doi.org/10.1038/s41598-022-20929-7

Download citation

Received: 01 May 2022

Accepted: 21 September 2022

Published: 03 October 2022

DOI: https://doi.org/10.1038/s41598-022-20929-7

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.